Code

Segment

Main Physical Properties

Special Features

Referential Dosage

Meg Thick 501

Synthetic Thickener for Pigment Printing

Appearance: Milky white viscous emulsion 

Composition : Acrylic acid multi-component copolymer

Ionicity: Anionic

pH value (1% solution) : 6.0~7.0

●Good water holding property, electrolyte resistance, clear shape and non flashing.

●Can get high color value, bright and full color.

●Soft handle

●High paste rate and rapidly in preparing paste.

●Very convenient to use, can directly add to pigment.

1.4-1.6%

Meg Thick 521

Appearance: Milky white viscous emulsion 

Composition : Acrylic acid multi-component copolymer

Ionicity: Anionic

pH value (1% solution) : 6.0~7.0

●Concentrate product adopting some imported raw materials, grafting brightening and salt-resistant group on the basis of the original thickener;

● Being applicable to pigment printing on all kinds of fabrics with clear shape, high color value, good thickening performance and good salt-resistance.

1.2-1.5%

Meg Thick 506

Synthetic Thickener for Disperse Printing

Appearance: Light grey white viscous emulsion

Ionicity: Anionic

pH value (1% solution): 6.0~7.0

Composition: Acrylic acid multi-component copolymer

● Replace sodium alginate to make printing paste which can obviously improve brightness, color value and clear shape and reduce the cost comparing with sodium alginate.

●Can completely substitute gums and sodium alginate, which provides better thickening effect, good stability, clear shape and good penetration performance.

●Easily wash off, soft handle.

●Convenient use at any time, rapid in preparing paste.

4-5%

Meg Thick 508

Synthetic Thickener for Reactive Printing

Appearance: milky white viscous emulsion

Ionicity: anionic

pH value (1% solution): 6.0~7.0

Composition: acrylic acid multi-component copolymer

●Used for thickening reactive printing paste; also used in conjunction with sodium alginate, reactive dye, sodium bicarbonate, resist salt and sodium hexametaphosphate with very good anti-electrolyte performance and thickening effect.

●High color value and bright color, clear shape and good comprehensive properties, such as permeability leveling property, etc.

●Rapid in preparing paste, convenient to use and paste remains steady.

●High rate of de-starch, soft handle.

●Excellent net penetration and leveling, flow performance.

4-4.5%

Meg Bond 340

Printing Binder

Appearance: Milky white with blue emulsion

Ionicity: Anionic

PH (30% solution):7.0-8.0

●Being suitable for pigment of all kinds fabrics, also for roller, rotary screen, flat screen, hand printing and stencil printing and other technology;

●For cotton, cotton coat, knitwear, terry fabrics and silk products have good applicability;

● Belongs to a new generation of environmentally friendly products, the film is transparent and colorless, high solid content, in conventional adhesives based on research and development of a new generation of environmentally friendly binder for pigment printing, printing dyeing rate is extremely high, and soft hand feeling, bright, soap wash, dry, wet friction degree are higher than those of traditional adhesive, non stick back, clear outline.

70-90%

Meg Bond 308

Component: Acrylic polymer copolymer

Ionicity: Anionic

PH value: 6.5-7.5

Viscosity: 5000-15000mpa·s

● A type of special binder with good affinity for PET glitterpowder and strong binding force with fabrics, which is suitable for special printing of cotton and polyester.

●After processing, it has good fastness, transparency and unique luster style of metal.

●The binder film is colorless and transparent, which will not darken the glitters, and can maintain the unique luster of the glitter slice.

●The water resistance of the film is very good.

●Higher binding strength, after printing, the fabrics can get very good dry and wet color fastness and brushing fastness.

●Good permeability, good leveling, and easy to conduct.

70-90%